What are the welding requirements of straight seam steel pipe？

 　　What are the weld requirements for straight seam steel pipes?

　　1. The height of the weld burr of the electric resistance welded steel pipe (ERW pipe)

　　The external burrs of the steel pipe welds should be removed, and the remaining height should not be greater than 0.5mm.

　　According to the request of the buyer, after negotiation between the supplier and the buyer, and specified in the contract, the burrs in the weld of the steel pipe can be removed. After the internal burr of the weld is removed, the remaining height should not be greater than 1.5mm; when the wall thickness is not greater than 4mm, the depth of the scraping groove after removing the internal burr should not be greater than 0.2mm; when the wall thickness is greater than 4mm, the depth of the scraping groove should not be greater than 0.4mm.

　　2. Remaining height of weld of submerged arc welded steel pipe (LSAW pipe)

　　When the wall thickness is not greater than 12.5mm, the internal and external weld reinforcement that exceeds the original surface contour of the steel pipe should not be greater than 3.2mm; when the wall thickness is greater than 12.5mm, the internal and external weld reinforcement that exceeds the original surface contour of the steel pipe should be Not more than 3.5mm. The super-high part of the weld reinforcement is allowed to be ground.

　　3. Wrong side

　　For electric resistance welded steel pipes, the mirror image misalignment of the edge of the steel strip at the weld is not allowed to make the remaining height on both sides less than 90% of the wall thickness of the steel pipe.

　　For submerged arc welded steel pipes, when the wall thickness is not greater than 12.5mm, the radial misalignment of the edge of the steel strip at the weld should not be greater than 1.6mm; when the wall thickness is greater than 12.5mm, the radial misalignment of the edge of the steel strip at the weld The side should not be greater than 0.125 times the wall thickness of the steel pipe.

　　4. Steel strip butt weld

　　Spiral seam submerged arc welded steel pipes (SSAW pipe) are allowed to have steel strip butt welds, but the distance between the connection point of the steel strip butt weld and the spiral seam and the pipe end should be greater than 150mm. When the steel strip butt weld is located at the pipe end, the spiral with the corresponding pipe end There should be a circumferential spacing of 150mm between the welds.

　　http://www.xysteelpipe.com/info/What-are-the-welding-requirements-of-straight-seam-steel-pipe%EF%BC%9F-1898-1.htm

评论

发表评论

此博客中的热门博文

SMLS steel pipe for Tanzania Gas pipeline project

图片
Project location: Tanzania Product：SMLS steel pipe Specification：168.3mm*14.27mm*SDR Standard and material：API 5L X52N PSL2 Application: Gas pipeline project In the last week of September, we received a new inquiry from regular customer who stated that it would take 4 weeks for delivery, including anti-corrosion. We learned that the fast delivery is most important point for this order. Xinyue people responded the fastest. Due to this order is for X52N PSL2 G high-grade seamless pipes, the stock quantity cannot meet the quantity of the entire order. With the strong resource integration ability of Xinyue, we found the production schedule of the steel pipe factory within 3 days and quickly organized new production. The customer arranges full process supervision from end customers, contractor customers, intermediate customers, and third parties from raw materials to the factory. During the supervision process of steel pipe production, they all witness the online UT test, Hydrostatic test, ...
阅读全文

Treatment method of steel pipe welding slag inclusion

What is welding slag inclusion? Welded pipe slag inclusions are slag that remains inside the weld. Welding slag inclusions are generally divided into two categories: The first category is metal slag inclusions. The second category is non-metallic slag, which refers to the slag remaining in the weld after welding, including electrode coating or flux, sulfide, oxide and nitride. According to its formation, it can be divided into point-like slag inclusions, linear slag inclusions, chain-like slag inclusions and dense slag inclusions. Slag inclusions will reduce the plasticity and toughness of steel pipe welds, and slag inclusions with sharp corners will cause stress concentration at the tip, and the tip will develop into a crack source, especially in welds with a large tendency to air quenching. Under the action of stress on the steel pipe, cracks will first appear at the slag inclusions in the weld and develop along the way, resulting in a decrease in strength and cracking of the weld. T...
阅读全文

ERW Steel Pipe Deliver to Argentina for oil and gas pipeline

图片
Project location：Argentina Product：ERW Steel Pipe Standard and material：API 5L PSL2 46th GR.X60M Specifications： OD: 457.2mm WT: 9.52mm Lenght:12M Application：oil and gas pipeline In the steel industry, customer demands vary, but quality and delivery time are always the most critical factors. Recently, Xinyue successfully provided a high-quality ERW pipe solution for a customer, and the entire process took only half a month, perfectly demonstrating our ability to respond quickly and execute efficiently. Although the customer’s order quantity was small, the steel grade requirements for the pipes were very high, and the supplier had to be listed in the client’s approved supplier directory. Facing such strict requirements, Xinyue mobilized all available resources and actively engaged with major suppliers. Ultimately, we successfully sourced BaoSteel’s inventory, which perfectly met the steel grade and quality requirements, and ensured on-time delivery. From receiving the inquiry to finali...
阅读全文